Our site saves small pieces of text information (cookies) on your device in order to deliver better content and for statistical purposes. You can disable the usage of cookies by changing the settings of your browser. By browsing our site without changing the browser settings you grant us permission to store that information on your device.
FATEN ADEL ISMAEL CHAQMAQCHEE1,*
The quaternary of GaAsSbN capping layer (CL) and GaAsSb/GaAsN CL InAs/GaAs quantum dots (QDs) and the GaInNAs/GaAs quantum wells (QWs) VCSEL samples were grown by molecular beam epitaxy (MBE). Photoluminescence (PL) measurement was performed for InAs/GaAs QDs with two different CLs at low temperature, while PL was carried out for GaInNAs/GaAs QWs VCSELs at various temperatures. In addition, Integrated intensity of electroluminescence (EL) for the QWs VCSEL were measured under continuous-wave (CW) and pulsed conditions to reach emission wavelength at around wavelength of λ=1.28 μm for optoelectronics applications. Thus, a low temperature red shift was achieved using GaAsSbN CL and InAs/GaAs QD but in low intensity. In addition, amplification was observed by QWs devices at low temperature of T=77K..
VCSEL, InAs/GaAs QDs, GaInNAs QWs, Photoluminescence, Electroluminescence, MBE.
FATEN ADEL ISMAEL CHAQMAQCHEE, InAs/GaAs QDs and dilute nitride QWs VCSELs grown by molecular beam epitaxy, Optoelectronics and Advanced Materials - Rapid Communications, 10, 5-6, May-June 2016, pp.364-367 (2016).
Submitted at: June 25, 2015
Accepted at: June 9, 2016
Optoelectronics and Advanced Materials - Rapid Communications
(2022): 0.5 - 2022 Journal Citation Reports (Clarivate Analytics, 2023)
Active accounts were imported to the new platform and assigned a random password by default. In order to access your account you need to access the login page and go through the Lost Password dialog (involves the system sending you an email with instructions) in order to reset your password. This step is necessary as passwords are kept in hashed form and the new platform uses modern hashing algorithms incompatible with the previous ones.