Our site saves small pieces of text information (cookies) on your device in order to deliver better content and for statistical purposes. You can disable the usage of cookies by changing the settings of your browser. By browsing our site without changing the browser settings you grant us permission to store that information on your device.
RENPING CAO1,* , YUJIAO YE1, QIYING PENG1, SILING GUO1, ZUOFU HU1, WEN HU1, HUI AO1, XIAOGUANG YU1
BaMgAl 10 O 17 :Mn 4+4+, K phosphor is synthesized by solid state method in air Emission spectrum in the region from 600 to 780 nm is observed with the strong emission peak at ~ 663 nm owing to the 2E → 4A2 transition of Mn4+ ions. Excitation spectrum in the range of 220 - 520 nm monitored at 663 nm is shown with three excitation band peaks ~ 288, 360, and 450 nm T he emission intensity of BaMgAl 10 O 17 :Mn 4+ phosphor is enhanced 1. 6 times by co doping K ion The luminous mechanism is explained by Tanabe-Sugano diagram of Mn 4+ ion.
Phosphors, Mn4+ ion, Red-emitting, Charge compensation.
RENPING CAO, YUJIAO YE, QIYING PENG, SILING GUO, ZUOFU HU, WEN HU, HUI AO, XIAOGUANG YU, Luminescence properties and charge compensation of BaMgAl 10 O 17 :Mn 4+4+, K red emitting phosphor, Optoelectronics and Advanced Materials - Rapid Communications, 12, 1-2, January-February 2018, pp.71-75 (2018).
Submitted at: April 26, 2017
Accepted at: Feb. 12, 2018
Optoelectronics and Advanced Materials - Rapid Communications
(2023): 0.5 - 2023 Journal Citation Reports (Clarivate Analytics, 2024)
Active accounts were imported to the new platform and assigned a random password by default. In order to access your account you need to access the login page and go through the Lost Password dialog (involves the system sending you an email with instructions) in order to reset your password. This step is necessary as passwords are kept in hashed form and the new platform uses modern hashing algorithms incompatible with the previous ones.