Our site saves small pieces of text information (cookies) on your device in order to deliver better content and for statistical purposes. You can disable the usage of cookies by changing the settings of your browser. By browsing our site without changing the browser settings you grant us permission to store that information on your device.
M. PETROVIĆ1,* , M. ROMČEVIĆ1, R. KOSTIĆ1, N. ROMČEVIĆ1, W. D. DOBROWOLSKI2, M. GILIĆ1, B. HADŽIĆ1, J. TRAJIĆ1, D. STOJANOVIĆ1, Z. LAZAREVIĆ1
Cd1 xMnxS nanoparticles (x=0.05 0.4) with average particle size of about 2.2nm were synthesized using the colloidal chemistry method and characterized by Raman scattering measurements. The dominant Raman line of Cd1 xMnxS nanoparticles was at about 300cm1 showing asymmetric broadening for ω<300cm1. Significant change in the line intensity for different Mn content x and excitation wavelength λ was noticed..
Nanostructured materials, Semiconductors, Optical properties, Raman spectroscopy.
M. PETROVIĆ, M. ROMČEVIĆ, R. KOSTIĆ, N. ROMČEVIĆ, W. D. DOBROWOLSKI, M. GILIĆ, B. HADŽIĆ, J. TRAJIĆ, D. STOJANOVIĆ, Z. LAZAREVIĆ, Optical properties of Cd1-xMnxS nanoparticles: off-resonance Raman spectroscopy, Optoelectronics and Advanced Materials - Rapid Communications, 10, 3-4, March-April 2016, pp.177-179 (2016).
Submitted at: Feb. 4, 2015
Accepted at: April 5, 2016
Optoelectronics and Advanced Materials - Rapid Communications
(2023): 0.5 - 2023 Journal Citation Reports (Clarivate Analytics, 2024)
Active accounts were imported to the new platform and assigned a random password by default. In order to access your account you need to access the login page and go through the Lost Password dialog (involves the system sending you an email with instructions) in order to reset your password. This step is necessary as passwords are kept in hashed form and the new platform uses modern hashing algorithms incompatible with the previous ones.