Our site saves small pieces of text information (cookies) on your device in order to deliver better content and for statistical purposes. You can disable the usage of cookies by changing the settings of your browser. By browsing our site without changing the browser settings you grant us permission to store that information on your device.
MIN QIN1, SHENGLI XIE1,* , YANFENG ZHU1, XIAOTONG XU1, JIANXIA GOU1,*
Transition metal selenide as supercapacitor electrode materials has been extensively studied and exhibits promising electrochemical performance. However, the poor cycling durability affects its practical application. Here, a design for the fabrication of nickel-cobalt selenide is presented. ZIF-67 was firstly synthesized and then the Ni element was introduced to fabricated precursor, which was then converted into selenides by hydrothermal reaction, in the presence of selenium powder and sodium borohydride. Results show that molar ratio of Co/Ni influences the crystalline phase, particles dispersion state and properties of the obtained selenides. The selenide obtained at optimized molar ratio of Co/Ni (1/1) shows high specific capacitance (1234.2 F g-1 at current density of 1 A g-1 ) and excellent cycling durability (76.0 % of the specific capacitance after 10000 cycles). The outstanding performance may be due to the proper composition and microstructure brought out by the proper Co and Ni molar ratio.
Nickel-cobalt selenide, Supercapacitor, Electrochemical properties.
MIN QIN, SHENGLI XIE, YANFENG ZHU, XIAOTONG XU, JIANXIA GOU, Preparation of Ni-Co selenide as long-cycling electrode material of supercapacitor, Optoelectronics and Advanced Materials - Rapid Communications, 16, 5-6, May-June 2022, pp.269-273 (2022).
Submitted at: Feb. 15, 2022
Accepted at: June 6, 2022
Optoelectronics and Advanced Materials - Rapid Communications
(2022): 0.5 - 2022 Journal Citation Reports (Clarivate Analytics, 2023)
Active accounts were imported to the new platform and assigned a random password by default. In order to access your account you need to access the login page and go through the Lost Password dialog (involves the system sending you an email with instructions) in order to reset your password. This step is necessary as passwords are kept in hashed form and the new platform uses modern hashing algorithms incompatible with the previous ones.