Our site saves small pieces of text information (cookies) on your device in order to deliver better content and for statistical purposes. You can disable the usage of cookies by changing the settings of your browser. By browsing our site without changing the browser settings you grant us permission to store that information on your device.
LING GAO1,2, LIAN ZHOU2, CHENGSHAN LI2, JIANQING FENG2, YAFENG LU2,*
Structural development was systematically studied in Zr1-xMnxO2-δ(x = 0~0.5) prepared at the sintering temperature of 1400℃ in Ar for 12h. It is found that the Mn ions go into the crystal lattice of ZrO2 to form a solid solution without any other compounds formed. After post treatment in high oxygen partial pressure, the cubic phase transforms into the monoclinic phase. We believe that the high symmetry phase can be retained to room temperature due to the effects of vacancy compensation and lattice distortion..
Oxides, Phase transformations, Microstructure.
LING GAO, LIAN ZHOU, CHENGSHAN LI, JIANQING FENG, YAFENG LU, Structure evolution of manganese stabilized zirconia, Optoelectronics and Advanced Materials - Rapid Communications, 6, 1-2, January-February 2012, pp.178-182 (2012).
Submitted at: Dec. 15, 2011
Accepted at: Feb. 20, 2012
Optoelectronics and Advanced Materials - Rapid Communications
(2023): 0.5 - 2023 Journal Citation Reports (Clarivate Analytics, 2024)
Active accounts were imported to the new platform and assigned a random password by default. In order to access your account you need to access the login page and go through the Lost Password dialog (involves the system sending you an email with instructions) in order to reset your password. This step is necessary as passwords are kept in hashed form and the new platform uses modern hashing algorithms incompatible with the previous ones.