Our site saves small pieces of text information (cookies) on your device in order to deliver better content and for statistical purposes. You can disable the usage of cookies by changing the settings of your browser. By browsing our site without changing the browser settings you grant us permission to store that information on your device.
J. ZHAN1,* , G. M. CHEN1, Q. ZHANG1
In the study, on the basis of good anticorrosion capability about silicate glass, silicate glass coating was sprayed by High Velocity Oxygen Fuel(HVOF) and corrosion mechanism in 36% HCl and 10 mol/L NaOH solution were studied. Scanning Electron Microscope(SEM), Energy Dispersive X-Ray analysis(EDX), X-Ray Diffraction(XRD) and corrosion dip experiment were carried out to study coating composition and corrosion process. The result shows that silicate glass coating is entirely noncrystallizable. Silicate glass coating has good anticorrosion capability in the condition of thick hydrochloric acid and strong canstic. The corrosion mechanism of silicate glass coating is similar to glass.
HVOF, Silicate glass coating, Corrosion, Alkali metals.
J. ZHAN, G. M. CHEN, Q. ZHANG, Study on the corrosion mechanism of HVOF silicate glass coating in 36% HCl and 10 mol/L NaOH solution, Optoelectronics and Advanced Materials - Rapid Communications, 4, 8, August 2010, pp.1170-1173 (2010).
Submitted at: June 23, 2010
Accepted at: Aug. 12, 2010
Optoelectronics and Advanced Materials - Rapid Communications
(2023): 0.5 - 2023 Journal Citation Reports (Clarivate Analytics, 2024)
Active accounts were imported to the new platform and assigned a random password by default. In order to access your account you need to access the login page and go through the Lost Password dialog (involves the system sending you an email with instructions) in order to reset your password. This step is necessary as passwords are kept in hashed form and the new platform uses modern hashing algorithms incompatible with the previous ones.