Our site saves small pieces of text information (cookies) on your device in order to deliver better content and for statistical purposes. You can disable the usage of cookies by changing the settings of your browser. By browsing our site without changing the browser settings you grant us permission to store that information on your device.

Synthesis and spectroscopic characterisation of LiFePO4 cathode materials

Z. LAZAREVIĆ1,* , G. KRIŽAN2,3, J. KRIŽAN4, M. MITRIĆ5, N. PAUNOVIĆ1, A. MILUTINOVIĆ1, N. ROMČEVIĆ1

Affiliation

  1. Institute of Physics, University of Belgrade, Pregrevica 118, 11080 Belgrade, Serbia
  2. Department of Materials Chemistry, National Institute of Chemistry, Ljubljana, Slovenia
  3. Faculty of Chemistry and Chemical Technology, University of Ljubljana, Ljubljana, Slovenia
  4. AMI d.o.o., Trstenjakova ulica 5, Ptuj, Slovenia
  5. Institute of Nuclear Sciences Vinča, University of Belgrade, Belgrade, Serbia

Abstract

Lithium iron phosphate (LiFePO4) are synthesized in complete and incomplete combustion and calcined at 700°C. The obtained samples were characterized by XRD, IR spectroscopy and magnetic measurement. Morphology of samples was controlled by SEM. The aim of this work is to show that it is possible to achieve a desired crystal phase by pulse combustion in a relatively cheap and fast way. The extremely rapid synthesis of almost pure phase material is possible due to the reduction in size of interacting particles and to an enormous number of collisions between them as a result of the strong turbulent flow associated with explosive combustion..

Keywords

Lithium iron phosphate, IR spectroscopy, Magnetic measurements.

Citation

Z. LAZAREVIĆ, G. KRIŽAN, J. KRIŽAN, M. MITRIĆ, N. PAUNOVIĆ, A. MILUTINOVIĆ, N. ROMČEVIĆ, Synthesis and spectroscopic characterisation of LiFePO4 cathode materials, Optoelectronics and Advanced Materials - Rapid Communications, 13, 3-4, March-April 2019, pp.228-234 (2019).